Chitosan fibrous scaffolds for cartilage tissue engineering

Cartilage tissue engineering;chitosan scaffold;Chondrocyte;Mesenchymal stem cell;chondrogenesis;cell adhesion

Ragetly, Guillaume R.

关键词: Cartilage tissue engineering;    chitosan scaffold;    Chondrocyte;    Mesenchymal stem cell;    chondrogenesis;    cell adhesion;   

Others  :  https://www.ideals.illinois.edu/bitstream/handle/2142/16781/2_Ragetly_Guillaume.pdf?sequence=4&isAllowed=y

美国|英语

来源: The Illinois Digital Environment for Access to Learning and Scholarship

【 摘 要 】

The biocompatibility of chitosan and its similarity with glycosaminoglycans make it attractive for cartilage engineering despite its limited cell adhesion properties. Structural and chemical characteristics of chitosan scaffolds may be improved for cartilage engineering application. We planned to evaluate chitosan meshes produced by a novel technique and the effect of chitosan structure on mesenchymal stem cells (MSCs) chondrogenesis. Another objective was to improve cell adhesion and chondrogenesis on chitosan by modifying the chemical composition of the scaffold (reacetylation, collagen II, or hyaluronic acid (HA) coating).A replica molding technique was developed to produce chitosan meshes of different fiber-width. A polyglycolic acid (PGA) mesh served as a reference. Constructs were analyzed at two and 21 days after seeding chondrocytes with confocal microscopy, scanning electron microscopy, histology, and quantitative analysis (weights, DNA, glycosaminoglycans, collagen II). Chondrocytes maintained their phenotypic appearance and a high viability but attached preferentially to PGA. Matrix production per chondrocyte was superior on chitosan. Chitosan meshes and sponges were analyzed after seeding and culture of MSCs under chondrogenic condition for 21 days. The cellularity was similar between groups but matrix production was greater on meshes.Chitosan and reacetylated-chitosan scaffolds were coated with collagen II or HA. Scaffolds were characterized prior to seeding MSCs. Chitosan meshes were then coated with collagen at two densities. PGA served as a reference. Constructs were evaluated after seeding or culture of MSCs for 21 days in chondrogenic medium. MSCs adhered less to reacetylated-chitosan despite collagen coating. HA did not affect cell adhesion. The cell attachment on chitosan correlated with collagen density. The cell number and matrix production were improved after culture in collagen coated meshes.The differences between PGA and chitosan are likely to result from the chemical composition. Chondrogenesis is superior on chitosan meshes compared to sponges. Collagen II coating is an efficient way to overcome poor cell adhesion on chitosan. These findings encourage the use of chitosan meshes coated with collagen II and confirm the importance of biomimetic scaffolds for tissue engineering. The decreased cell adhesion on reacetylated chitosan and the poor mechanical stability of PGA limit their use for tissue engineering.