Coated stainless steel 441 as interconnect material for solid oxide fuel cells: Oxidation performance and chromium evaporation

JOURNAL OF POWER SOURCES

卷:248

Article

Grolig, J. G.¹  Froitzheim, J.¹  Svensson, J. -E.¹ 

[1] Chalmers Univ Technol, SE-41296 Gothenburg, Sweden

关键词: Interconnect;    Chromium volatilization;    AISI 441;    Reactive elements;    SOFC;   

DOI  :  10.1016/j.jpowsour.2013.08.089

来源: Elsevier

【 摘 要 】

Reactive Element (RE) and RE/cobalt-coated stainless steel AISI 441 was exposed at Solid Oxide Fuel Cell (SOFC) cathode conditions (850 degrees C in air with 3% water content) for up to 500 h. The chromium evaporation was measured by applying the denuder technique. Uncoated material exhibited severe spallation which could be successfully prevented by using cerium or lanthanum coatings. By applying double layer coatings of cerium or lanthanum in combination with cobalt the oxidation rate was decreased and the chromium volatilisation was also about 90% lower than the uncoated material. (C) 2013 The Authors. Published by Elsevier B.V. All rights reserved.

【 授权许可】

Free