Anisotropic magnetization, specific heat and resistivity of RFe2Ge2 single crystals

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS

卷:270

Article

Avila, MA ; Bud'ko, SL ; Canfield, PC

关键词: magnetically ordered materials;    X-ray diffraction;    magnetic measurements;    heat capacity;    electronic transport;   

DOI  :  10.1016/S0304-8853(03)00672-3

来源: Elsevier

【 摘 要 】

We have grown RFe2Ge2 single crystals for R=Y and ten members of the lanthanide series (Pr, Nd, Sm, Gd-Tm, Lu) using Sn flux as the solvent. The method yields clean, high quality crystal plates as evidenced by residual resistivities and RRR values in the range of 3-12 muOmegacm and 20-90, respectively. The crystals are also virtually free of magnetic impurities or secondary phases, allowing the study of the intrinsic anisotropic magnetic behavior of each compound. Characterization was made with X-Ray diffraction, and temperature and field-dependent magnetization, specific heat and resistivity. Very strong anisotropies arising mostly from CEF effects were observed for all magnetic rare earths except Gd. Antiferromagnetic ordering occurred at temperatures between 16.5K (Nd) and 1.1 K (Ho) that roughly scale with the de Gennes factor for the heavy rare earths. For some members there is also a lower temperature transition associated with changes in the magnetic structure. Tm did not order down to 0.4K, and appears to be a van Vleck paramagnet. All members which ordered above 2K showed a metamagnetic transition at 2K for fields below 70 kOe. The calculated effective moments per rare earth atom are close to the expected free ion values of R3+ except for Sm which displays anomalous behavior in the paramagnetic state. The non-magnetic members of this series (Y, Lu) are characterized by an unusually large electronic specific heat coefficient (gamma similar to 60 mJ/mol K-2) and temperature-independent susceptibility term (chi(0) similar to 0.003 emu/mol), indicative of a relatively large density of states at the Fermi surface. (C) 2003 Elsevier B.V. All rights reserved.

【 授权许可】

Free