Microstructure and activity of Pd catalysts prepared on commercial carbon support for the liquid phase decomposition of formic acid
Article
关键词: HYDROGEN-PRODUCTION;    DEHYDROGENATION;    METAL;    NANOPARTICLES;    GENERATION;    SIZE;    PARAMETERS;    EFFICIENT;    OXIDE;    XPS;   
DOI  :  10.1016/j.ijhydene.2022.10.149
来源: SCIE
【 摘 要 】

In this work, a series of Pd catalysts supported on commercially available activated carbon (Norit (R)) were prepared by employing different metal precursors (Pd(NO3)2 and Na2PdCl4) by the impregnation-reduction method at different pH. Catalysts were tested for the liquid phase decomposition of formic acid to generate hydrogen. The best results, in terms of small particle size and high catalytic activity were achieved for the Pd/C sample prepared by using Pd(NO3)2 salt impregnated at pH = 2.5, and reduced with sodium borohydride. The particle size of the best Pd/C catalyst is (4.1 +/- 1.4) nm with initial TOFs of 2929 and 683 h-1 at 60 and 30 degrees C respectively and an apparent activation energy of 40 kJ mol-1. Samples prepared by using Na2PdCl4 precursor, consisted of particles with higher size and thus lower activity than the ones prepared with Pd(NO3)2. Regardless the Pd precursor employed, the best results in terms of particle size and activity were achieved at the point of zero charge of the support when the Pd species and the carbon surface were both neutral. The impregnation pH not only determines the particle size, but also the nature of the reducing agent does. The catalytic activity was shown to be size-dependent and it was shown that a mixture of surface Pd0 and PdII oxidation states is beneficial for the activity. When comparing with literature catalysts with similar composition, we found that our best catalyst is competitive enough and that Norit (R) support could be promising for future studies on this reaction.(c) 2022 The Author(s). Published by Elsevier Ltd on behalf of Hydrogen Energy Publications LLC. This is an open access article under the CC BY-NC-ND license (http:// creativecommons.org/licenses/by-nc-nd/4.0/).

【 授权许可】

Free   

  文献评价指标  
  下载次数:0次 浏览次数:1次