Recyclable magnetite-silver heterodimer nanocomposites with durable antibacterial performance

Bioactive Materials

卷:3

关键词: Heterodimeric nanostructure;    Antibacterial;    Chitosan coating;    Silver nanoparticle;    Recyclable;   

DOI  :  10.1016/j.bioactmat.2017.05.008

来源: DOAJ

【 摘 要 】

There is a significant need for magnetite-silver nanocomposites that exhibit durable and recyclable antimicrobial activity. In this study, magnetic iron oxide nanoparticles (Fe3O4 NPs) coated with ethylenediamine-modified chitosan/polyacrylic acid copolymeric layer (Fe3O4@ECS/PAA) were fabricated. Subsequently, directly deposited silver (Ag) NPs procedure was carried out to form the antibacterial heterodimers of Fe3O4@ECS/PAA-Ag NPs. The composition and morphology of the resultant nanostructures were confirmed by FT-IR, XRD, TEM and TGA. The overall length of the heterodimers was approximately 45 nm, in which the mean diameter of Fe3O4@ECS/PAA NPs reached up to 35 nm, and that of Ag NPs was around 15 nm. The mass fraction of silver NPs in the nanocomposites was about 63.1%. The obtained Fe3O4@ECS/PAA NPs exhibited good colloidal stability, and excellent response to additional magnetic field, making the NPs easy to recover after antibacterial tests. In particular, the Fe3O4@ECS/PAA-Ag NPs retained nearly 100% biocidal efficiency (106–107 CFU/mg nanoparticles) for both Gram-negative bacteria E. coli and Gram-positive bacteria S. aureus throughout ten cycles without washing with any solvents or water, exhibiting potent and durable antibacterial activity.

【 授权许可】

Unknown