期刊论文详细信息
Materials Research
Oxidation and erosion-oxidation behavior of steels
Stela Maria De Carvalho Fernandes1  Olandir Vercino Correa1  Lalgudi Venkataraman Ramanathan1 
[1] ,Instituto de Pesquisas Energéticas e NuclearesSão Paulo SP ,Brazil
关键词: oxidation;    erosion;    erosion-oxidation;    wastage;    steels;   
DOI  :  10.1590/S1516-14392008000100008
来源: SciELO
PDF
【 摘 要 】

The high temperature oxidation and erosion-oxidation (E-O) behavior of steels AISI 1020, 304, 310, and 410 were determined. These steels were selected to evaluate the effect of chromium content on its E-O resistance. The oxidation behavior was determined in a thermogravimetric analyzer. A test rig in which a specimen assembly was rotated through a fluidized bed of erodent particles was used to determine the E-O behavior. Alumina powder (200 µm) was used as the erodent. The E-O tests were carried out in the temperature range 25-600 °C, with average particle impact velocities of 3.5 and 15 ms-1 and impact angle of 90°. The oxidation resistance of the steels increased with chromium content. The E-O behavior of the steels was determined as wastage. The E-O wastage of the steels exposed to particle impact at low velocity was low but increased with temperature above 300 °C. The E-O wastage of the different steels exposed to particle impact at high velocity was quite similar. The wastage increased with increase in temperature above 500 °C. The increases in E-O wastage of the steels observed at temperatures above 300, 400 or 500 °C, depending on the steel, were due mainly to a transition in the dominant wastage process, from 'erosion' to 'erosion-oxidation'.

【 授权许可】

CC BY   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License

【 预 览 】
附件列表
Files Size Format View
RO202005130152353ZK.pdf 710KB PDF download
  文献评价指标  
  下载次数:15次 浏览次数:21次