Role of vanadium in Bi-2223 ceramics

Pramana

D R Mishra¹  S V Sharma¹  R G Sharma¹ 

[1] National Physical Laboratory, Dr K.S. Krishnan Road, New Delhi 110 012, India$$

关键词: Superconductors;    crystal growth;    X-ray diffraction;    magnetic properties.;   

DOI  :  

学科分类：物理（综合）

来源: Indian Academy of Sciences

【 摘 要 】

The effect of substitution of vanadium in Bi1.6Pb0.4Sr2Ca2Cu3O𝛿 ceramic at Bi and Cu sites has been investigated for the resistivity, a.c. susceptibility, XRD and a.c. magnetization studies. Enhancement in 𝑇𝑐 for the smaller concentrations of V at either of the two sites was observed which followed an expected lattice distortion and decrease in 𝑇𝑐 for higher V concentrations. V plays a role of substituting element more than just a sintering agent as reflected in the more rapid decrease in 𝑇𝑐 at Cu-site and further in the magnetization values that are higher compared to the values at the Bisite. It indicates higher magnetization scattering at the Cu site. The results were explained keeping in mind the liquid phase mechanism behind the formation of the 2223 phase and the possibility of magnetic scattering.

【 授权许可】

Unknown