Parameters Affecting the Mechanical Properties of Fly Ash-Based Geopolymer Binders _ Experimental Results

Euroinvent ICIR 2018

Lzrescu, A.^1,2 ; Szilagyi, H.^1 ; Ioani, A.^2 ; Baer, C.^3

N.I.R.D. URBAN-INCERC, Cluj-Napoca Branch, Romania^1

Technical University of Cluj-Napoca, Faculty of Civil Engineering, Romania^2

N.I.R.D. URBAN-INCERC, Timioara Branch, Romania^3

关键词: Alkaline activation;    Alkaline activators;    Environment friendly;    Geopolymer binders;    Local raw materials;    Main parameters;    Ordinary Portland cement;    Solid material;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/374/1/012035/pdf
DOI  :  10.1088/1757-899X/374/1/012035

来源: IOP

【 摘 要 】

As the demand for concrete and the needs to satisfy development of infrastructure facilities increase, it is essential to find alternatives to create environment-friendly concrete. The particular procedure of alkaline activation of fly ash - in which ash resulting from a power plant is combined with a specific alkaline activator in order to create a solid material, then dried at a certain temperature - opened new opportunities for this new material to get attention worldwide. In order to obtain a material with similar properties of ordinary Portland cement concrete and to obtain desirable compressive strengths, the parameters that affect this type of binders should be fully understood. The aim of this paper is to study the main parameters affecting the mechanical strength of the fly ash-based geopolymer paste and their interactions. Parameters such as molarity of sodium hydroxide (from 8M to 12M) and alkaline activators ratio (from 0,5 to 2,5) were analysed to observe how they affect the mechanical properties of the geopolymer paste. Experimental results show that the compressive strength of the fly ash-based geopolymer paste produced using Romanian local raw materials increases with the increase of the concentration of sodium hydroxide and higher ratios of Na2SiO3/NaOH solution.