Aluminum Coating Influence on Nitride Layer Performance Deposited by MO-CVD in Fluidized Bed on Austenitic Stainless Steel Substrate

Euroinvent ICIR 2018

Gluc, D.G.^1 ; Perju, M.C.^1 ; Nejneru, C.^1 ; Burduhos Nergi, D.D.^1 ; Lzrescu, I.E.^1

Technical University Gheorghe Asachi of Iasi-Romania, Department of Technologies and Equipments for Materials Processing, Blvd. Mangeron, No. 51, Iasi

700050, Romania^1

关键词: Aluminum thin films;    Austenitic stainless;    Chemical compositions;    Intelligent solutions;    Nitriding treatment;    Thermochemical treatments;    Treatment techniques;    Triisobutylaluminum;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/374/1/012020/pdf
DOI  :  10.1088/1757-899X/374/1/012020

来源: IOP

【 摘 要 】

The modification of surface properties by duplex treatments, involving the overlapping of two surface treatment techniques, has been established as an intelligent solution to create new applications for the substrate metallic material. There are driveline components operating under very tough wear and corrosion conditions, with high temperature and humidity variations. Such components are usually made of high Cr and Ni stainless steel and for the hardening of surfaces it is recommended a thermo chemical treatment. Since stainless steels, especially austenitic stainless steels, are difficult to nitride, experimental studies focus on increasing the depth of the nitride layer and surface hardness. Achieving the goal involves changing active layer chemical composition by introducing aluminum in the surface layer. In order to find a solution, a new surface treatment technique is produced by combining aluminum thin films by MO-CVD in a fluidized bed using a triisobutylaluminum precursor with a thermo chemical nitriding treatment.