Ceramics based on zirconium dioxide stabilized with indium oxide and praseodymium oxide

3rd International Youth Scientific Forum with International Participation "New Materials"

Frolova, M.G.^1 ; Kargin, Yu F.^1 ; Lukin, E.S.^2 ; Popova, N.A.^2 ; Lysenkov, A.S.^1 ; Titov, D.D.^1 ; Ivicheva, S.N.^1

Baykov Institute of Metallurgy and Material Science RAS, Moscow, Russia^1

Mendeleyev University of Chemical Technology of Russia, Moscow, Russia^2

关键词: Co deposition;    Indium oxide;    Open porosity;    Physicochemical property;    Praseodymium oxides;    Zirconium dioxide;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/347/1/012027/pdf
DOI  :  10.1088/1757-899X/347/1/012027

来源: IOP

【 摘 要 】

The solid solutions based on Zirconia doped with indium oxide and praseodymium oxide with different concentration was obtained by the method of inverse heterophase co-deposition. The physico-chemical properties of obtained samples were examined. The highest properties have been achieved in samples of the composition Zr1-xRxO2-δ (R=23 mol .% In). This composition has a density of 5.38 g/cm3; open porosity is 0 %, the bending strength is 203 MPa.