Comparative Studies on microstructure, mechanical and corrosion behaviour of DMR 249A Steel and its welds

International Conference on Recent Advances in Materials, Mechanical and Civil Engineering

材料科学;机械制造;土木建筑工程

Mohammed, Raffi^1 ; Dilkush^2 ; Madhusudhan Reddy, G.^4 ; Srinivasa Rao, K.^3

Department of Metallurgical and Materials Engineering, NIT, Andhra Pradesh, India^1

Department of Metallurgical and Materials Engineering, RGUKT, Nuzvid, India^2

Department of Metallurgical Engineering, Andhra University, Visakhapatnam, India^3

Defence Metallurgical Research Laboratory, Hyderabad, India^4

关键词: 3.5% nacl solutions;    Comparative studies;    Corrosion behaviour;    Gas tungsten arc welding;    Microstructural changes;    Shielded metal arc welding;    Structural component;    Universal testing machines;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/330/1/012018/pdf
DOI  :  10.1088/1757-899X/330/1/012018

来源: IOP

【 摘 要 】

DMR249A Medium strength (low carbon) Low-alloy steels are used as structural components in naval applications due to its low cost and high availability. An attempt has been made to weld the DMR 249A steel plates of 8mm thickness using shielded metal arc welding (SMAW) and gas tungsten arc welding (GTAW). Welds were characterized for metallography to carry out the microstructural changes, mechanical properties were evaluated using vickers hardness tester and universal testing machine. Potentio-dynamic polarization tests were carried out to determine the pitting corrosion behaviour. Constant load type Stress corrosion cracking (SCC) testing was done to observe the cracking tendency of the joints in a 3.5%NaCl solution. Results of the present study established that SMA welds resulted in formation of relatively higher amount of martensite in ferrite matrix when compared to gas tungsten arc welding (GTAW). It is attributed to faster cooling rates achieved due to high thermal efficiency. Improved mechanical properties were observed for the SMA welds and are due to higher amount of martensite. Pitting corrosion and stress corrosion cracking resistance of SMA welds were poor when compared to GTA welds.