Alternative welding reconditioning solutions without post welding heat treatment of pressure vessel

5th ModTech International Conference - Modern Technologies in Industrial Engineering

Cicic, D.T.^1 ; Rontescu, C.^1 ; Bogatu, A.M.^1 ; Dijmrescu, M.C.^1

University POLITEHNICA of Bucharest, Materials Technology and Welding Department, 313 Splaiul Independentei, Bucharest

060042, Romania^1

关键词: Controlled deposition;    Hardness variation;    High temperature and high pressure;    Post-weld heat treated;    Post-welding heat treatments;    Welding repairs;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/227/1/012025/pdf
DOI  :  10.1088/1757-899X/227/1/012025

来源: IOP

【 摘 要 】

In pressure vessels, working on high temperature and high pressure may appear some defects, cracks for example, which may lead to failure in operation. When these nonconformities are identified, after certain examination, testing and result interpretation, the decision taken is to repair or to replace the deteriorate component. In the current legislation it's stipulated that any repair, alteration or modification to an item of pressurised equipment that was originally post-weld heat treated after welding (PWHT) should be post-weld heat treated again after repair, requirement that cannot always be respected. For that reason, worldwide, there were developed various welding repair techniques without PWHT, among we find the Half Bead Technique (HBT) and Controlled Deposition Technique (CDT). The paper presents the experimental results obtained by applying the welding reconditioning techniques HBT and CDT in order to restore as quickly as possible the pressure vessels made of 13CrMo4-5. The effects of these techniques upon the heat affected zone are analysed, the graphics of the hardness variation are drawn and the resulted structures are compared in the two cases.