Effect of PWHT on Microstructure, Mechanical and Corrosion Behaviour of Gas Tungsten Arc Welds of IN718 Superalloys

International Conference on Recent Advances in Materials, Mechanical and Civil Engineering

材料科学;机械制造;土木建筑工程

Dilkush^1 ; Mohammed, Raffi^2 ; Madhusudhan Reddy, G.^3 ; Srinivasa Rao, K.^4

Department of Metallurgical and Materials Engineering, RGUKT, Nuzvid, India^1

Department of Metallurgical and Materials Engineering, NIT Andhra Pradesh, India^2

Department of Metallurgical Engineering, Andhra University, Visakhapatnam, India^3

Defence Metallurgical Research Laboratory, Hyderabad, India^4

关键词: Gas tungsten arc welding;    Gas tungsten arc welds;    Microstructural changes;    Microstructure changes;    Nickel- based superalloys;    Post weld heat treatment;    Post-weld heat treated;    Vickers microhardness;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/330/1/012030/pdf
DOI  :  10.1088/1757-899X/330/1/012030

来源: IOP

【 摘 要 】

The present work aims to improve corrosion resistance and mechanical behavior of the welds with suitable post weld heat treatment i.e. direct aging and solutionizing treatments (980STA, 1080STA). Gas tungsten arc welding (GTAW) has been performed on Inconel 718 (IN718) nickel based super alloy plates with 3mm thickness. The structural -property relationship of the post weld heat treated samples is judged by correlating the microstructural changes with observed mechanical behavior and pitting corrosion resistance of the welds As-recevied, direct aging (DA), 980STA,1080STA were studied. Welds were characterized for microstructure changes with scanning electron microscopy (SEM) and optical microscopy (OM).Vickers micro- hardness tester was used to measure the hardness of the weldments. Potential-dynamic polarization testing was carried out to study the pitting corrosion resistance in 3.5%NaCl (Sodium chloride) solution at 30°C.Results of the present study established that post weld heat treatments resulted in promoting the element segregation diffusion and resolve them from brittle laves particles in the matrix. Increased precipitation of strengthening phases lead to a significant increase in fusion zone hardness of 1080STA post weld heat treated condition compared to as welded, direct aged, 980STA conditions. Due to significant changes in the microstructural behavior of 1080STA condition resulted in superior pitting corrosion resistance than 980STA, direct aged and as- recevied conditions of IN718 GTA welds.