Effect of bench time polymerization on depth of cure of dental composite resin

Innovation in Polymer Science and Technology 2016

材料科学;化学

Harahap, K.^1 ; Yudhit, A.^1 ; Sari, F.^1

Faculty Dentistry, Universitas Sumatera Utara, Medan, Indonesia^1

关键词: Blue light;    Composite resins;    Control groups;    Dental composite resins;    Depth of cure;    Nanofiller composites;    One-way anova;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/223/1/012062/pdf
DOI  :  10.1088/1757-899X/223/1/012062

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

The aim of this research was to investigate the effect of bench time before light cured polymerization on the depth of cure of dental composite resin. Nanofiller composite resin (Filtek Z350 XT,3M, ESPE,China) was used in this study. Sixty samples of nanofiller composite resin were made and divided into control and test groups with bench time for 0, 15, 30, 45, and 60 min. For the test group, composite resins were stored in refrigerator with 4°C temperatures. Meanwhile, for the control groups, the composite resin was stored at room temperature. The samples were prepared using metal mould with size diameter of 6 mm and 4 mm in thickness. Samples were cured for 20 s by using visible blue light curing unit. Part of samples that unpolymerized were removed by using a plastic spatula. The remaining parts of samples were measured by digital caliper and noted as depth of cure (mm). Data were analyzed to one-way ANOVA and LSD tests (p≤0.05). Results showed there was no significance differences between test groups (p=0.5). A 60 minutes bench time group showed the highest depth of cure value among test group, and it was almost similar with control group value. It can be concluded that longer bench time can increase the depth of cure of composite resin.