Design and Characterization of Renewable Bioasphalt Containing Damar Resin, Fly Ash, Wasted Cooking Oil and Latex

International Conference on Advanced Materials for Better Future 2016

Setyawan, A.^1 ; Djumari^1 ; Legowo, S.J.^1 ; Widiharjo, B.^1 ; Zai, A.K.S.^1 ; Pradana, A.A.W.^1 ; Rusadi, I.P.^1 ; Permana, A.^1

Roadmate Research Group, Civil Engineering Department, Sebelas Maret University, Jl. Ir. Sutami 36 A, Solo

57126, Indonesia^1

关键词: Basic composition;    Natural resins;    Optimal composition;    Optimum composition;    Penetration test;    research methods;    Softening points;    Solubility test;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/176/1/012027/pdf
DOI  :  10.1088/1757-899X/176/1/012027

来源: IOP

【 摘 要 】

Dasphalt is one alternative of bioasphalt, made from materials that can be renewed as a substitute for conventional asphalt. Dasphalt inspired from jabung made of damar resin, brick powder and wasted cooking oil. Jabung have the same character with conventional asphalt. Research has been conducted by the characteristics of jabung but there are still many shortcomings, softening point and ductility values are not qualify. In this research the brick powder will be replaced by fly ash, as fly ash has a finer grain so that it can become a better absorbent. The resin will act as a natural resin for dasphalt, wasted cooking oil will be a mixed solvent. Use of additional polymers latex, is expected to improve the elasticity of dasphalt in ductility test. The purpose of this study was to determine the nature of the modification dasphalt properties in accordance with the specifications of asphalt penetration test and find the optimal composition of dasphalt. This research method is done by direct testing in the laboratory. In the present study that became the basic composition of the resin is resin (100g pure resin+ 350g resin packaging or powder), fly ash (150g) and wasted cooking oil (205g) and latex were mixed at temperatures below 150°C. While variations of latex starting from 0%, 2%, 4%, 6%, 8% and 10%. Several asphalt characterization are performed include penetration tests, test softening point, ductility test, flash point test, specific gravity test, affinity test and solubility test. Dasphalt modification achieved optimum composition of resin (100g pure resin or resin chunk + 350Gr packaging), Fly Ash powder (150g), cooking oil (205g), and latex 4%, ductility increased from 63.5 cm to 119.5 cm, the value of the flash point was originally at temperature of 240°C to 260°C, dasphalt penetration from 68.2 dmm to 43 dmm, and the value of density decreases to 1.01 g/cm3to 0.99 g/cm3. Dasphalt modifications meet some of the specifications and could be categorized as bitumen penetration 40.