会议论文详细信息
5th International Congress on Energy Fluxes and Radiation Effects 2016 | |
Luminescence of ultrafine magnesium oxide ceramics with deep traps | |
Nikiforov, S.V.^1 ; Kortov, V.S.^1 ; Kiryakov, A.N.^1 ; Petrovykh, K.A.^1 | |
Ural Federal University, Ekaterinburg, Russia^1 | |
关键词: Deep traps; F-type centers; Grain size; High dose; Pulse electron beams; Reducing conditions; Trapping centers; Ultrafine; | |
Others : https://iopscience.iop.org/article/10.1088/1742-6596/830/1/012135/pdf DOI : 10.1088/1742-6596/830/1/012135 |
|
来源: IOP | |
【 摘 要 】
Thermoluminescence (TL) of ultrafine anion-defective magnesium oxide ceramics with a grain size of about 150 nm, which were thermally treated in highly reducing conditions at T=1100-1400 °C, has been studied after high-dose irradiation with a pulse electron beam (130 keV). Thermal treatment was found to cause TL intensity grow, which is associated with an increasing concentration of F-type centers. It was shown that varying occupancy of deep trapping centers changes a yield of the TL peak at 380 K. A hypothesis was made that the traps which are responsible for the TL peak at 380 K mainly have a hole nature in the samples under study.【 预 览 】