1020 steel coated with Ti/TiN by Cathodic Arc and Ion Implantation

8th International Congress of Engineering Physics

物理学;工业技术

Bermeo, F.^1 ; Quintana, J.P.^2,3 ; Kleiman, A.^2,3 ; Sequeda, F.^4 ; Márquez, A.^2,3

Universidad Santiago de Cali, Cali, Colombia^1

Universidad de Buenos Aires, Facultad de Ciencias Exactas y Naturales, Departamento de Física, Buenos Aires, Argentina^2

Universidad de Buenos Aires, Consejo Nacional de Investigaciones Científicas y Técnicas, Instituto de Física Del Plasma (INFIP), Facultad de Ciencias Exactas y Naturales, Buenos Aires, Argentina^3

Universidad Del Valle, Cali, Colombia^4

关键词: Cathodic arc;    Corrosion performance;    Mechanical and tribological properties;    Nitrogen environment;    Steel substrate;    Ti/TiN film;    Tribological properties;    Young modulus;   

Others  :  https://iopscience.iop.org/article/10.1088/1742-6596/792/1/012061/pdf
DOI  :  10.1088/1742-6596/792/1/012061

学科分类：工业工程学

来源: IOP

【 摘 要 】

TiN coatings have been widely studied in order to improve mechanical properties of steels. In this work, thin Ti/TiN films were prepared by plasma based immersion ion implantation and deposition (PBII&D) with a cathodic arc on AISI 1020 steel substrates. Substrates were exposed to the discharge during 1 min in vacuum for the deposition of a Tiunderlayer with the aim of improving the adhesion to the substrate. Then, a TiN layer was deposited during 6 min in a nitrogen environment at a pressure of 3xl0-4mbar. Samples were obtained at room temperature and at 300 °C, and with or without ion implantation in order to analyze differences between the effects of each treatment on the tribological properties. The mechanical and tribological properties of the films were characterized. The coatings deposited by PBII&D at 300 °C presented the highest hardness and young modulus, the best wear resistance and corrosion performance.