International Physics Conference at the Anatolian Peak 2016 | |
Effect of annealing on photovoltaic performance of fabricated planar organic-inorganic perovskite solar cells | |
Baltakesmez, Ali^1,2 ; Biber, Mehmet^1 ; Tüzemen, Sebahattin^1 | |
Department of Physics, Faculty of Science, Atatürk University, Erzurum | |
25240, Turkey^1 | |
Department of Physics, Faculty of Science, Çankiri Karatekin University, Çankiri | |
18100, Turkey^2 | |
关键词: Annealing procedures; Current voltage curve; Effect of annealing; Electron transport; Investigate effects; Optical intensities; Photo-voltaic efficiency; Photovoltaic performance; | |
Others : https://iopscience.iop.org/article/10.1088/1742-6596/707/1/012024/pdf DOI : 10.1088/1742-6596/707/1/012024 |
|
来源: IOP | |
【 摘 要 】
We fabricated planar perovskite solar cells used CH3NH3PbI3-xClxfor light harvesting to investigate effect of annealing on photovoltaic performance of fabricated device. The devices have an architecture of Glass/ITO/Pedot:PSS/Perovskite/PC61BM/Al. Layers of hole transport (Pedot:PSS), active and electron transport (PC61BM) were prepared from solution based one step deposition method by a spin coater and standard annealing procedure. The current-voltage curves of devices were measured inside the glovebox using a Keithley 2400 sourcemeter. The cells were illuminated by a solar simulator have optical intensity value of 300 mW/cm2. For the best cells, while PCE value of 5.78% before the annealing, photovoltaic efficiency was improved average 13% delivered a short-circuit current density of 3.20 mA/cm2, open-circuit voltage of 0.82 V and fill factor of 0.74, leading to an efficiency of 6.54% with respect to prior to annealing.