Effects of Laser Repetition Rate on the Structural and Superconducting Properties of YBCO films Deposited by PLD on NiW Tapes

11th European Conference on Applied Superconductivity

Liu, Linfei^1 ; Xiao, Guina^1 ; Xu, Da^1 ; Wang, Ying^1 ; Wu, Xiang^1 ; Luo, Qiang^1 ; Li, Yijie^1

Key Laboratory of Artificial Structures and Quantum Control (Ministry of Education), Department of Physics and Astronomy, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai

200240, China^1

关键词: Experimental conditions;    Four-probe methods;    High quality;    Island density;    Island size;    Laser repetition rate;    Structural and superconducting properties;    YBa2Cu3O7-X;   

Others  :  https://iopscience.iop.org/article/10.1088/1742-6596/507/2/022015/pdf
DOI  :  10.1088/1742-6596/507/2/022015

来源: IOP

【 摘 要 】

YBa2Cu3O7-x(YBCO) films were fabricated at various laser repetition rates on CeO2/YSZ/CeO2buffered Ni-W tapes by pulsed laser deposition (PLD). The dependence of structural and superconducting properties on the laser repetition rates was investigated. The microstructure and surface morphology of YBCO films were characterized by X-ray diffraction and atomic force microscopy. And the critical current (Ic) of YBCO films was measured by the conventional four-probe method. The results show that with increasing laser repetition rate the island density decreased and the island size increased. It was found that the texture and Icof YBCO films were largely dependent on the laser repetition rate. And furthermore it was observed that the film thickness was not in directly proportional to laser repetition rate. Under optimum experimental condition, high quality YBCO films with critical current Icabove 500 A/cm at 77 K and 0T were obtained.