Development of a wear-resistant flux cored wire of Fe-C-Si-Mn-Cr-Ni-Mo-V system for deposit welding of mining equipment parts

International Scientific and Research Conference on Knowledge-based Technologies in Development and Utilization of Mineral Resources 2017

矿业工程;地球科学

Osetkovsky, I.V.^1 ; Kozyrev, N.A.^1 ; Kryukov, R.E.^1 ; Usoltsev, A.A.^1 ; Gusev, A.I.^1

Siberian State Industrial University, 42 Kirova Street, Novokuznetsk

654007, Russia^1

关键词: Aluminum production;    Austenite grain;    Chemical compositions;    Flux-cored wire;    Laboratory conditions;    Metallographic analysis;    Non-metallic inclusions;    Powdered materials;   

Others  :  https://iopscience.iop.org/article/10.1088/1755-1315/84/1/012017/pdf
DOI  :  10.1088/1755-1315/84/1/012017

来源: IOP

【 摘 要 】

The effect of introduction of cobalt in the charge of the flux cored wire of Fe-C-Si-Mn-Cr-Ni-Mo-V system operating under abrasive and abrasive-shock loads is studied. In the laboratory conditions samples of flux cored wires were made, deposition was performed, the effect of cobalt on the hardness and the degree of wear was evaluated, metallographic studies were carried out. The influence of cobalt introduced into the charge of the flux cored wire of Fe-C-Si-Mn-Cr-Ni-Mo-V system on the structure, nature of nonmetallic inclusions, hardness and wear resistance of the weld metal was studied. In the laboratory conditions samples flux cored wire were made using appropriate powdered materials. As a carbon-fluorine-containing material dust from gas cleaning units of aluminum production was used. In the course of the study the chemical composition of the weld metal was determined, metallographic analysis was performed, mechanical properties were determined. As a result of the metallographic analysis the size of the former austenite grain, martensite dispersion in the structure of the weld metal, the level of contamination with its nonmetallic inclusions were established.