Biologically reinforced geopolymer composites

Geopolymer;Composite;Biological;Cork;Abaca

Roper, Daniel Steven ; Kriven ; Waltraud M.

关键词: Geopolymer;    Composite;    Biological;    Cork;    Abaca;   

Others  :  https://www.ideals.illinois.edu/bitstream/handle/2142/97271/ROPER-THESIS-2017.pdf?sequence=1&isAllowed=y

美国|英语

来源: The Illinois Digital Environment for Access to Learning and Scholarship

【 摘 要 】

A series of studies detailing the characteristics of biologically reinforced geopolymers is presented.Cork particle reinforced sodium geopolymer composites were shown to have a maximum flexural strength of 2.5 MPa, and an average strain-to-failure of 0.75%.Abaca fiber reinforced sodium geopolymer composites had flexural strengths exceeding 25 MPa.The main focus of this study was abaca fiber reinforced potassium geopolymer composites, which had flexural strengths exceeding 50 MPa at 8 wt% abaca fibers.This new composite was shown to have good water and saltwater durability, decent sodium hydroxide and freeze cycle durability, and poor sulfuric acid durability.The composite was also tested for heat sensitivity, and showed a steady decrease in flexural strength as it was exposed to higher temperatures.The composite was unable to carry any load after being treated to 300°C.Weibull statistical analysis was used to better understand the range of flexural strengths within different sample groups.Finally, SEM analysis was employed to characterize fracture surfaces and mode of failure in the different sample sets.