Characterization of Corrosion Behavior of Alloy 22 Regarding its Lifetime Performance as a Potential Nuclear Waste Container Material.

Rebak, R. B. ; McCright, R. D.

Technical Information Center Oak Ridge Tennessee

关键词: Corrosion;    Nuclear waste containers;    Nevada;    Performance evaluation;    Stress corrosion cracking;   

RP-ID  :  DE200515013494

学科分类：工程和技术（综合）

美国|英语

来源: National Technical Reports Library

【 摘 要 】

Alloy 22 (UNS N06022) was proposed for the corrosion resistant outer barrier of a two-layer waste package container for nuclear waste at the potential repository site at Yucca Mountain in Nevada (USA). A testing program is underway to characterize and quantify three main modes of corrosion that may occur at the site. Current results show that the containers would perform well under general corrosion, localized corrosion and environmentally assisted cracking (EAC). For example, the general corrosion rate is expected to be below 100 nm/year and the container is predicted to be outside the range of potential for localized corrosion and environmentally assisted cracking.