In this study the loading capacities of selected actinides onto some of the most common sorbent materials which are present in caustic nuclear waste storage tanks have been determined. Some of these transition metal oxides and activated carbons easily absorb or precipitate plutonium, neptunium and even uranium, which if care is not taken may lead to unwanted accumulation of some of these fissile materials in nuclear waste tanks during waste processing. Based on a caustic synthetic salt solution simulant bearing plutonium, uranium and neptunium and ''real'' nuclear waste supernate solution, the loading capacities of these actinides onto iron oxide (hematite), activated carbon and anhydrous sodium phosphate have been determined. The loading capacities for plutonium onto granular activated carbon and iron oxide (hematite) in a caustic synthetic salt solution were, respectively, 3.4 0.22 plus or minus and 5.5 plus or minus 0.38 microgram per gram of sorbent. The loading capacity for plutonium onto a typical nuclear waste storage tank sludge solids was 2.01 microgram per gram of sludge solids. The loading capacities for neptunium onto granular activated carbon and iron oxide (hematite) in a caustic synthetic salt solution were, respectively, 7.9 plus or minus 0.52 and greater than 10 microgram per gram of sorbent. The loading capacity for neptunium onto a typical nuclear waste storage tank sludge solids was 4.48 microgram per gram of sludge solids. A typical nuclear waste storage tank solid material did not show any significant affinity for uranium. Sodium phosphate showed significant affinity for both neptunium and uranium, with loading capacities of 6.8 and 184.6 plus or minus 18.5 microgram per gram of sorbent, respectively.
PDF
download
878987797
028-85220240