Preparation of nickel substrates for coated conductors.

Truchan, T. G. ; Rountree, F. H. ; Lanagan, M. T. ; McClellan, S. M. ; Miller, D. J.

Technical Information Center Oak Ridge Tennessee

关键词: Nickel;    Substrates;    High-tc superconductors;    Annealing;    Grain growth;   

RP-ID  :  DE2001768570

学科分类：工程和技术（综合）

美国|英语

来源: National Technical Reports Library

【 摘 要 】

Polycrystalline Ni has been used as a substrate for high-current, coated YBa(sub 2)Cu(sub 3)O(sub x) superconductors. For many conductors, Ni is rolled to large deformation and annealed to produce a cube texture. In this study, Ni was rolled to greater than 95% reduction and annealed in 5% H(sub 2)/95% He at 300-1000 C for various times. The resulting substrates were examined by scanning electron microscopy, X-ray and electron diffraction, and surface interferometry. Key determinations for the Ni were extent of in-plane and out-of-plane texture, surface smoothness, and grain size. The extent of texture was approximately independent of annealing temperature and increased slightly with annealing time. Annealing at temperatures greater than 600 C increased surface roughness, primarily due to grain-boundary grooving. Grain growth was fastest at 1000 C and was proportional to time to the 0.1 power.