Screening of two additively manufactured liquid injector designs was conducted in the UAH high pressure spray facility. Four variants of each geometry with slightly different dimensions were obtained from eleven separate commercial additive manufacturing services. The devices were manufactured from Inconel 625 using the selective laser melting (SLM) powder bed process. The devices were cold flowed with water over a range of relevant pressure drops (75 psi to 1500 psi) to produce water flow rates from 0.037 to 1.75 lbm/s into ambient back pressure. Discharge coefficients determined from the testing along with the associated uncertainties provide insight into characteristic flow performance variabilities that can be expected from the SLM process for similar geometries.