Friction and Wear of Unlubricated NiTiHf with Nitriding Surface Treatments

Stanford, Malcolm K

关键词: FRICTION;    WEAR;    COEFFICIENT OF FRICTION;    INTERMETALLICS;    NICKEL ALLOYS;    NITRIDING;    SURFACE TREATMENT;    PLASMAS (PHYSICS);    PROTECTION;    MODULUS OF ELASTICITY;    HARDNESS;    BINARY ALLOYS;    BEARINGS;    GEARS;   

RP-ID  :  NASA/TM-2018-219740,E-19460,GRC-E-DAA-TN49310

美国|英语

来源: NASA Technical Reports Server

【 摘 要 】

The unlubricated friction and wear properties of the superelastic materials NiTi and NiTiHf, treated by either gas nitriding or plasma nitriding, have been investigated. Pin on disk testing of the studied materials was performed at sliding speeds from 0.01 to 1m/s at normal loads of 1, 5 or 10N. For all of the studied friction pairs (NiTiHf pins vs. NiTi and NiTiHf disks) over the given parameters, the steady-state coefficients of friction varied from 0.22 to 1.6. Pin wear factors ranged from approximately 1E-6 against the NiTiHf and plasma nitrided disks to approximately 1E-4 for the gas nitrided disks. The plasma nitrided disks provided wear protection in several cases and tended to wear by adhesion. The gas nitrided treatment generated the most pin wear but had essentially no disk wear except at the most severe of the studied conditions (1N load and 1m/s sliding speed). The results of this study are expected to provide guidance for design of components such as gears and fasteners.