Micromechanical Failure Analyses for Finite Element Polymer Modeling

CHAMBERS,ROBERT S. ; REEDY JR.,EARL DAVID ; LO,CHI S. ; ADOLF,DOUGLAS B. ; GUESS,TOMMY R.

Sandia National Laboratories

关键词: Calibration;    Stresses;    Polymers;    36 Materials Science;    Cavitation;   

DOI  :  10.2172/768081
RP-ID  :  SAND2000-2769
RP-ID  :  AC04-94AL85000
RP-ID  :  768081

美国|英语

来源: UNT Digital Library

【 摘 要 】

Polymer stresses around sharp corners and in constrained geometries of encapsulated components can generate cracks leading to system failures. Often, analysts use maximum stresses as a qualitative indicator for evaluating the strength of encapsulated component designs. Although this approach has been useful for making relative comparisons screening prospective design changes, it has not been tied quantitatively to failure. Accurate failure models are needed for analyses to predict whether encapsulated components meet life cycle requirements. With Sandia's recently developed nonlinear viscoelastic polymer models, it has been possible to examine more accurately the local stress-strain distributions in zones of likely failure initiation looking for physically based failure mechanisms and continuum metrics that correlate with the cohesive failure event. This study has identified significant differences between rubbery and glassy failure mechanisms that suggest reasonable alternatives for cohesive failure criteria and metrics. Rubbery failure seems best characterized by the mechanisms of finite extensibility and appears to correlate with maximum strain predictions. Glassy failure, however, seems driven by cavitation and correlates with the maximum hydrostatic tension. Using these metrics, two three-point bending geometries were tested and analyzed under variable loading rates, different temperatures and comparable mesh resolution (i.e., accuracy) to make quantitative failure predictions. The resulting predictions and observations agreed well suggesting the need for additional research. In a separate, additional study, the asymptotically singular stress state found at the tip of a rigid, square inclusion embedded within a thin, linear elastic disk was determined for uniform cooling. The singular stress field is characterized by a single stress intensity factor K{sub a} and the applicable K{sub a} calibration relationship has been determined for both fully bonded and unbended inclusions. A lack of interfacial bonding has a profound effect on inclusion-tip stress fields. A large radial compressive stress is generated in front of the inclusion-tip when the inclusion is well bonded, whereas a large tensile hoop stress is generated when the inclusion is unbended, and frictionless sliding is allowed. Consequently, an epoxy disk containing an unbended inclusion appears more likely to crack when cooled than a disk containing a fully bonded inclusion. A limited number of tests have been carried out to determine if encapsulant cracking can be induced by cooling a specimen fabricated by molding a square, steel insert within a thin, epoxy disk. Test results are in qualitative agreement with analysis. Cracks developed only in disks with mold-released inserts, and the tendency for cracking increased with inclusion size.