FINAL ANALYTICAL RESULTS FROM THE EXAMINATION OF CORROSION ON SECTIONS OF CORROSION PROBE REMOVED FROM TANK 241-AN-107 ON 08/10/2006

DUNCAN JB ; COOKE GA

关键词: AR FACILITIES;    CREVICE CORROSION;    PITTING CORROSION;    STORAGE FACILITIES;    CORROSION PRODUCTS;    EVALUATION;    RADIOACTIVE WASTE STORAGE;   

DOI  :  10.2172/940013
RP-ID  :  RPP-RPT-32425 Rev 0
PID  :  OSTI ID: 940013
Others  :  TRN: US0807069

美国|英语

来源: SciTech Connect

【 摘 要 】

Tank Farms Operations removed an electrochemical noise probe from Tank 241-AN-107. In the field, the probe was cut into four sections, wrapped, and placed in a 55-gallon drum, This drum was delivered to the 222-S Laboratory. The 222 S Laboratory unpackaged the sections of the AN-107 electrochemical noise probe and examined the material for evidence of corrosion. Each of the four sections contained three C-ring and three bullet specimens. The specimens were examined for pitting corrosion, crevice corrosion, and stress corrosion cracking. No evidence of stress corrosion cracking was found in the stressed C-ring specimens. Minor pitting was evident on some surfaces. Crevice corrosion was the dominant type of corrosion observed.