EFFECTS OF CHEMISTRY AND OTHER VARIABLES ON CORROSION AND STRESS CORROSION CRACKING IN HANFORD DOUBLE SHELL TANKS
BROWN MH
关键词: AR FACILITIES;    26;    HANFORD RESERVATION;    STORAGE FACILITIES;    PITTING CORROSION;    STRESS CORROSION;    CRACK PROPAGATION;    RADIOACTIVE WASTES;    CORROSIVE EFFECTS;   
DOI  :  10.2172/943299
RP-ID  :  RPP-RPT-37505 Rev 0
PID  :  OSTI ID: 943299
Others  :  TRN: US0900392
学科分类:核能源与工程
美国|英语
来源: SciTech Connect
PDF
【 摘 要 】

Laboratory testing was performed to develop a comprehensive understanding of the corrosivity of the tank wastes stored in Double-Shell Tanks using simulants primarily from Tanks 241-AP-105, 241-SY-103 and 241-AW-105. Additional tests were conducted using simulants of the waste stored in 241-AZ-102, 241-SY-101, 241-AN-107, and 241-AY-101. This test program placed particular emphasis on defining the range of tank waste chemistries that do not induce the onset of localized forms of corrosion, particularly pitting and stress corrosion cracking. This document summarizes the key findings of the research program.

【 预 览 】
附件列表
Files Size Format View
RO201705180000431LZ 53187KB PDF download
  文献评价指标  
  下载次数:5次 浏览次数:31次