Laser welding and post weld treatment of modified 9Cr-1MoVNb steel.

Xu, Z. (Nuclear Engineering Division)

关键词: ARC WELDING;    DEFECTS;    GLAZING MATERIALS;    HARDNESS;    HEAT AFFECTED ZONE;    LASER WELDING;    LASERS;    POROSITY;    STEELS;    TEMPERING;    TESTING;    WELDED JOINTS;   

DOI  :  10.2172/1037972
RP-ID  :  ANL/NE-12/12
PID  :  OSTI ID: 1037972
Others  :  TRN: US201208%%535

学科分类：材料科学（综合）

美国|英语

来源: SciTech Connect

【 摘 要 】

Laser welding and post weld laser treatment of modified 9Cr-1MoVNb steels (Grade P91) were performed in this preliminary study to investigate the feasibility of using laser welding process as a potential alternative to arc welding methods for solving the Type IV cracking problem in P91 steel welds. The mechanical and metallurgical testing of the pulsed Nd:YAG laser-welded samples shows the following conclusions: (1) both bead-on-plate and circumferential butt welds made by a pulsed Nd:YAG laser show good welds that are free of microcracks and porosity. The narrow heat affected zone has a homogeneous grain structure without conventional soft hardness zone where the Type IV cracking occurs in conventional arc welds. (2) The laser weld tests also show that the same laser welder has the potential to be used as a multi-function tool for weld surface remelting, glazing or post weld tempering to reduce the weld surface defects and to increase the cracking resistance and toughness of the welds. (3) The Vicker hardness of laser welds in the weld and heat affected zone was 420-500 HV with peak hardness in the HAZ compared to 240 HV of base metal. Post weld laser treatment was able to slightly reduce the peak hardness and smooth the hardness profile, but failed to bring the hardness down to below 300 HV due to insufficient time at temperature and too fast cooling rate after the time. Though optimal hardness of weld made by laser is to be determined for best weld strength, methods to achieve the post weld laser treatment temperature, time at the temperature and slow cooling rate need to be developed. (4) Mechanical testing of the laser weld and post weld laser treated samples need to be performed to evaluate the effects of laser post treatments such as surface remelting, glazing, re-hardening, or tempering on the strength of the welds.