Phase equilibria in the Co-Mn-Ni system

JOURNAL OF ALLOYS AND COMPOUNDS

卷:777

Article

Zhou, Yang^1,2  Nash, Philip²  Dai, Xingye^2,3  Li, Dongnan^2,4  Silva, Alexandre Alves²  Cardoso, Gabriel Ribeiro Lopes² 

[1] Shanghai Jiao Tong Univ, Shanghai Key Lab Adv High Temp Mat & Precis Formi, 800,Dongchuan Rd, Shanghai 200240, Peoples R China

[2] IIT, Thermal Proc Technol Ctr, Chicago, IL 60616 USA

[3] Beijing Inst Technol, Beijing 100081, Peoples R China

[4] Fujian Univ Technol, Coll Mat Sci & Engn, Fuzhou 350118, Fujian, Peoples R China

关键词: High-temperature alloys;    Phase transitions;    X-ray diffraction;    Magnetic measurements;    Thermal analysis;   

DOI  :  10.1016/j.jallcom.2018.11.087

来源: Elsevier

【 摘 要 】

Co-Mn-Ni alloys are promising shape memory alloys and functional materials. However, very limited information can be found regarding the phase transformations and magnetic properties in this ternary system. In this work, a series of 22 Co-Mn-Ni alloys with various compositions were selected and synthesized based on a computed phase diagram. Metallography, X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), differential scanning calorimetry (DSC), hardness and Gleeble tests were used for microstructural characterization and phase transformation investigations. The results indicate that all samples show a face-centered-cubic (FCC) structure after quenching from 1000 degrees C. Phase transformations and Curie temperatures of the samples were obtained through a combined method of analyzing the heat effects and thermogravimetric behavior of the alloys in the presence of a magnetic field during differential scanning calorimetry. Thermal expansion tests indicate that the FCC to BCC transformation is a thermoelastic transformation whereas the shape memory effect was not observed in the Co-Mn-Ni alloys tested. (C) 2018 Elsevier B.V. All rights reserved.