ThMn12-type structure and uniaxial magnetic anisotropy in ZrFe10Si2 and Zr1-xCexFe10Si2 alloys

JOURNAL OF ALLOYS AND COMPOUNDS

卷:657

Article

Gabay, A. M.¹  Hadjipanayis, G. C.¹ 

[1] Univ Delaware, Dept Phys & Astron, Newark, DE 19716 USA

关键词: Intermetallics;    Permanent magnets;    Crystal structure;    Anisotropy;   

DOI  :  10.1016/j.jallcom.2015.10.073

来源: Elsevier

【 摘 要 】

Arc-melted (Zr1-xCex)(1.1)Fe10Si2 alloys were found to crystallize into a pure or nearly pure ThMn12 structure for 0 <= x <= 0.6. At room temperature, the alloys exhibit ferromagnetism with an uniaxial magnetocrystalline anisotropy. Metastable ZrFe10Si2 compound possesses room-temperature saturation magnetization of at least 11 kG and Curie temperature of 325 degrees C; both properties slightly decrease when Ce is being substituted for Zr. The anisotropy field, on the other hand, increases with the Ce from 16.9 to 24 kOe at x = 0.6. These intrinsic magnetic characteristics as well as the absence of expensive rare-earths and Co make the compounds interesting for development of low-cost permanent magnets. At 0.7 <= x <= 0.8, the ThMn12 structure was found to co-exist with the Th2Ni17-type structure, whereas the equilibrium Th2Zn17-type structure was observed only at x = 1. Prepared under similar conditions Hf1.1Fe10Si2 alloy does not crystallize into the ThMn12-type structure. (C) 2015 Elsevier B.V. All rights reserved.

【 授权许可】

Free