Improved-sensitivity integral SQUID magnetometry of (Ga,Mn)N thin films in proximity to Mg-doped GaN

JOURNAL OF ALLOYS AND COMPOUNDS

卷:868

Article

Gas, Katarzyna¹  Kunert, Gerd²  Dluzewski, Piotr¹  Jakiela, Rafal¹  Hommel, Detlef^2,3,4  Sawicki, Maciej¹ 

[1] Polish Acad Sci, Inst Phys, Aleja Lotnikow 32-46, PL-02668 Warsaw, Poland

[2] Univ Bremen, Inst Solid State Phys, Otto Hahn Allee 1, D-28359 Bremen, Germany

[3] Univ Wroclaw, Inst Expt Phys, M Borna 9, Wroclaw, Poland

[4] PORT Polish Ctr Technol Dev, Lukasiewicz Res Network, Stablowicka 147, Wroclaw, Poland

关键词: Magnetic films and multilayers;    Nitride materials;    Semiconductors;    Crystal growth;    Magnetization;    Magnetic measurements;   

DOI  :  10.1016/j.jallcom.2021.159119

来源: Elsevier

【 摘 要 】

Nominally 45 nm GaN:Mg / 5 nm (Ga,Mn)N / 45 nm GaN:Mg trilayers structures prepared by molecular beam epitaxy on GaN-buffered Al2O3 substrates are investigated to verify whether the indirect co-doping by holes from the cladding layers can alter the spin-spin interaction in (Ga,Mn)N. The four investigated structures, differing with the Mg doping level, are carefully characterized at a nanoscale by high-resolution transition electron microscopy (HRTEM), energy-dispersive x-ray spectroscopy, and secondary ion mass spectrometry. Importantly, HRTEM decisively excluded a presence of foreign Mn-rich phases. Magnetic studies of these structures are aided by the employment of a dedicated experimental approach of the in situ compensation of the magnetic contribution from the substrate, allowing an up to about fifty-fold reduction of this contribution. This technique, dedicated to these structures, simultaneously provides a tenfold reduction of long-term instabilities of the output of the magnetometer and lowers the experimental jitter to merely 5 x 10(-7) emu at 70 kOe, vastly increasing the precision and the credibility of the results of the standard integral (volume) superconducting quantum interference device magnetometry, particularly in high magnetic fields. The magnetic characteristics of the trilayer structures established here prove identical with the already known properties of the thick (Ga,Mn)N single layers, namely (i) the low temperature ferromagnetism among Mn3+ ions driven by superexchange and (ii) purely paramagnetic response at higher temperatures. The possible cause of the lack of any effects brought about by the adjacent Mg-doping is a presence of residual Mn in the cladding layers, resulting in the deactivation of the p-type doping intended there. This finding points out that a more intensive technological effort has to be exerted to promote the co-doping-driven carrier-mediated ferromagnetic coupling in Mn-enriched GaN, especially at elevated temperatures. (C) 2021 Elsevier B.V. All rights reserved.