Catalytic coatings on steel for low-temperature propane prereforming to solid oxide fuel cell (SOFC) application

JOURNAL OF COLLOID AND INTERFACE SCIENCE

卷:336

Article

Alphonse, Pierre¹  Ansart, Florence¹ 

[1] Univ Toulouse, CIRIMAT UPS, CNRS, F-31062 Toulouse 9, France

关键词: Coating;    Colloid;    PEG;    Steam reforming;    Fuel processing;   

DOI  :  10.1016/j.jcis.2009.04.079

来源: Elsevier

【 摘 要 】

Catalyst layers (4-20 mu m) of rhodium (1 wt%) supported on alumina, titania, and ceria-zirconia (Ce0.5Zr0.5O2) were coated on stainless-steel corrugated sheets by dip-coating in very stable colloidal dispersions of nanoparticles in water. Catalytic performances were studied for low-temperature (<= 500 degrees C) steam reforming of propane at a steam to carbon ratio equal to 3 and low contact time (approximate to 0.01 s). The best catalytic activity for propane steam reforming was observed for titania and ceria-zirconia supports for which propane conversion started at 250 degrees C and was more than three times better at 350 degrees C than conversion measured on alumina catalyst. For all catalysts a first-order kinetics was found with respect to propane at 500 degrees C. Addition of PEG 2000 in titania and ceria-zirconia sols eliminated the film cracking observed without additive with these supports. Besides, the PEG addition strongly expanded the porosity of the layers, so that full catalytic efficiency was maintained when the thickness of the ceria-zirconia and titania films was increased. (C) 2009 Elsevier Inc. All rights reserved.

【 授权许可】

Free