Thermal behaviour of arsenic trioxide adsorbed on activated carbon

JOURNAL OF HAZARDOUS MATERIALS

卷:166

Article

Cuypers, Frederic¹  De Dobbelaere, Christopher²  Hardy, An²  Van Bael, Marlies K.²  Helsen, Lieve¹ 

[1] Katholieke Univ Leuven, Dept Mech Engn, Div Appl Mech & Energy Convers, B-3001 Heverlee, Belgium

[2] Hasselt Univ, Inst Mat Res, Lab Inorgan & Phys Chem, B-3590 Diepenbeek, Belgium

关键词: Arsenic trioxide;    Activated carbon;    Desorption;    Thermogravimetric analysis;    Thermal stability;   

DOI  :  10.1016/j.jhazmat.2008.12.048

来源: Elsevier

【 摘 要 】

The thermal stability and desorption of arsenic trioxide (As2O3) adsorbed on activated carbon (AC) was investigated as this phenomenon is expected to influence the arsenic release during low temperature pyrolysis of chromated copper arsenate (CCA) wood waste. Firstly, a thermogravimetric (TG) experiment with arsenolite, an allotropic form of As2O3, was performed. The sample starts to sublime at temperatures lower than 200,C with a sublimation peak temperature of 271 degrees C. Subsequently, TG experiments with samples of As2O3 adsorbed on AC revealed that only very little (max. 6 +/- 3 wt%) As2O3 was volatilised at temperatures below 280 degrees C, while still 41.6 (+/- 5)wt% of the original arsenic concentration was retained at 440 degrees C and 28.5 (+/- 3) wt% at 600 degrees C. The major arsenic volatilisation occurred between 300 degrees C and 500 degrees C. The kinetic parameters of desorption, activation energy of desorption (E-d) and pre-exponential factor (A), were determined by fitting an Arrhenius model to the experimental data, resulting in E-d = 69 kJ/mol, A = 1.21 x 10(4) s(-1). It can be concluded that the adsorption of As2O3 on AC can contribute to the thermal stabilisation of As2O3, Consequently, during low temperature pyrolysis of CCA wood arsenic release may be prevented by adsorption of As2O3 on the coal-type product formed during the thermal decomposition of the wood. (C) 2008 Elsevier B.V. All rights reserved.