Electrochemical copper deposition from an ethaline-CuCl2•2H2O DES
Article
Ghosh, Swatilekha1  Roy, Sudipta1 
[1] Newcastle Univ, Merz Court, Sch Chem Engn & Adv Mat, Newcastle Upon Tyne NE2 7RU, Tyne & Wear, England
关键词: Choline chloride;    Ionic liquids;    Ethaline;    Copper deposition;    Electroplating;    Electrodeposition;   
DOI  :  10.1016/j.surfcoat.2013.10.069
来源: Elsevier
PDF
【 摘 要 】

Cu electroplating was carried out using a pure ethaline melt, a 1:2 ratio of choline chloride and ethylene glycol, at room temperature by potentiostatic and galvanostatic methods. Hydrated cupric chloride was added to the pure ethaline melt. Polarisation data for cupric ion reduction to copper was collected using an RDE to determine where metal deposition was feasible. Smooth Cu deposits were obtained at -4.7 x 10(-3) A/cm(2) using 0.2 M CuCl12 center dot 2H(2)O at 25 degrees C at a current efficiency of (95 +/- 5)% at a rotation speed of 700 rpm. XRD analysis of the deposit showed a polycrystalline face centred cubic structure with (111) texture. The crystalline size was 66 +/- 10 nm with some internal strain. EDX analysis showed the presence of carbon and chlorine with copper in the deposit, which was due to the break-down of the DES. Several deposition processes were carried out from a single bath to examine bath stability. The bath was found to be stable when a soluble anode was employed, and became unstable when an insoluble anode was used due to other reactions proceeding at the cathode. (C) 2013 Elsevier B.V. All rights reserved.

【 授权许可】

Free   

【 预 览 】
附件列表
Files Size Format View
10_1016_j_surfcoat_2013_10_069.pdf 1605KB PDF download
  文献评价指标  
  下载次数:3次 浏览次数:1次