APS TBC performance on directionally-solidified superalloy substrates with HVOF NiCoCrAlYHfSi bond coatings

SURFACE & COATINGS TECHNOLOGY

卷:284

Article

Lance, M. J.¹  Unocic, K. A.¹  Haynes, J. A.¹  Pint, B. A.¹ 

[1] Oak Ridge Natl Lab, Div Mat Sci & Technol, Oak Ridge, TN 37831 USA

关键词: Photo-stimulated luminescence piezospectroscopy (PLPS);    Water vapor;    Bond coating;    Alumina scale;    TBC;    Directionally-solidified superalloy;   

DOI  :  10.1016/j.surfcoat.2015.08.067

来源: Elsevier

【 摘 要 】

Directionally-solidified (DS) superalloy components with advanced thermal barrier coatings (TBC) to lower the metal operating temperature have the potential to replace more expensive single crystal superalloys for large land-based turbines. In order to assess relative TBC performance, furnace cyclic testing was used with superalloys 1483, X4 and Hf-rich DS 247 substrates and high velocity oxygen fuel (HVOF)-NiCoCrAlYHfSi bond coatings at 1100 degrees C with 1-h cycles in air with 10% H2O. With these coating and test conditions, there was no statistically-significant effect of substrate alloy on the average lifetime of the air plasma sprayed (APS) yttria-stabilized zirconia (YSZ) top coatings on small coupons. Using photo-stimulated luminescence piezospectroscopy maps at regular cycling intervals, the residual compressive stress in the alpha-Al2O3 scale underneath the YSZ top coating and on a bare bond coating was similar for all three substrates and delaminations occurred at roughly the same rate and frequency. X-ray fluorescence (XRF) measurements collected from the bare bond coating surface revealed higher Ti interdiffusion occurring with the 1483 substrate, which contained the highest Ti content. (C) 2015 Elsevier B.V. All rights reserved.

【 授权许可】

Free