Chromium nanostructures formed by dewetting of heteroepitaxial films on W(100)

Article

关键词: ULTRATHIN CR FILMS;    GROWTH;    TRANSITION;   

DOI  :  10.1103/PhysRevB.86.045454

来源: SCIE

【 摘 要 】

In this paper, we report the surprising formation of square-based facetted islands with linear dimension of the order of 500 nm upon dewetting of a Cr multilayer on W(100). We show that these square islands are composed of inclined facets surrounding a depressed center such that the facet slopes inward with the outer edges of the islands thicker than the centers. The islands' shapes do not represent traditional equilibrium crystal shapes as expected for a Wulf construction. In situ UV and x-ray photoelectron emission microscopy allied to spatially resolved spectroscopy throws considerable light on the nature of the dewetting and shows that the metal surface between the islands remains covered by a thin pseudomorphic wetting layer of similar to 1 ML. Low-energy electron diffraction and scanning tunneling and atomic force microscopies allow quantification of facet slopes, and we identify a predominance of tilted Cr(100) facets +/- 5 degrees off of the substrate normal bound by (210) planes at similar to 26 degrees. The epitaxial Cr islands adopt the bulk Cr lattice constant but are tilted with respect to the surface normal. We suggest that the Cr crystallite tilting creates a vicinal-like interface structure that determines the island morphology.

【 授权许可】

Free