Fabrication of polyester fabrics with tungsten bronze nanorods and a silane coupling agent for improved thermal storage and washing durability
Research
Ye-eun Woo1  Kyung Wha Oh2 
[1] Dept of Fashion, Graduate School, Chung-Ang University, 06974, Seoul, Republic of Korea;Dept. of Fashion, College of Art, Chung-Ang University, 17546, Anseong, Republic of Korea;
关键词: Tungsten bronze nanorods;    Outdoor sportswear;    Silane coupling agent;    Photothermal effect;    Washing durability;   
DOI  :  10.1186/s40691-022-00310-y
 received in 2021-11-26, accepted in 2022-06-28,  发布年份 2022
来源: Springer
PDF
【 摘 要 】

The thermal storage and washing durability of polyester fabrics treated with tungsten bronze nanorods(TBNRs) were analyzed to determine the optimal concentration for the photothermal effect in this study. TBNRs with an average length of 34.0 ± 2.5 nm and a diameter of 2.3 ± 0.4 nm were synthesized by the thermal decomposition of Ammonium metatungstate hydrate(AMT) in oleylamine (OA) to generate TBNRs that are capable of emitting heat by efficiently absorbing light in the near-infrared region. The effect of TBNR concentration and the silane coupling agent on the photothermal effect and washing durability of the PET fabric were evaluated with a solar simulator. As a result, as the concentration of TBNRs increased, the photothermal effect increased, and the maximum photothermal effect was shown at 5 wt%. In addition, washing durability were further improved by adding 0.5 wt% silane counpling agent. Overall, the post-processing treatment effectively increased the photothermal effect without a significant change in the physical properties and color of the polyester.

【 授权许可】

CC BY   
© The Author(s) 2022

【 预 览 】
附件列表
Files Size Format View
RO202305118373619ZK.pdf 1501KB PDF download
41116_2022_35_Article_IEq258.gif 1KB Image download
41116_2022_35_Article_IEq262.gif 1KB Image download
41116_2022_35_Article_IEq267.gif 1KB Image download
41116_2022_35_Article_IEq273.gif 1KB Image download
41116_2022_35_Article_IEq278.gif 1KB Image download
Fig. 1 64KB Image download
41116_2022_35_Article_IEq299.gif 1KB Image download
【 图 表 】

41116_2022_35_Article_IEq299.gif

Fig. 1

41116_2022_35_Article_IEq278.gif

41116_2022_35_Article_IEq273.gif

41116_2022_35_Article_IEq267.gif

41116_2022_35_Article_IEq262.gif

41116_2022_35_Article_IEq258.gif

【 参考文献 】
  • [1]
  • [2]
  • [3]
  • [4]
  • [5]
  • [6]
  • [7]
  • [8]
  • [9]
  • [10]
  • [11]
  • [12]
  • [13]
  • [14]
  文献评价指标  
  下载次数:6次 浏览次数:8次