Printed Strain Gauge on 3D and Low-Melting Point Plastic Surface by Aerosol Jet Printing and Photonic Curing

Sensors

Michela Borghetti¹  Mauro Serpelloni¹  Emilio Sardini¹ 

[1] Department of Information Engineering, University of Brescia, 25123 Brescia, Italy;

关键词: printed electronics;    aerosol jet printed;    photonic sintering;    strain gauges;    non-planar surfaces;    plastics;    temperature sensitive;    silver ink;   

DOI  :  10.3390/s19194220

来源: DOAJ

【 摘 要 】

Printing sensors and electronics directly on the objects is very attractive for producing smart devices, but it is still a challenge. Indeed, in some applications, the substrate that supports the printed electronics could be non-planar or the thermal curing of the functional inks could damage temperature-sensitive substrates such as plastics, fabric or paper. In this paper, we propose a new method for manufacturing silver-based strain sensors with arbitrary and custom geometries directly on plastic objects with curvilinear surfaces: (1) the silver lines are deposited by aerosol jet printing, which can print on non-planar or 3D surfaces; (2) photonic sintering quickly cures the deposited layer, avoiding the overheating of the substrate. To validate the manufacturing process, we printed strain gauges with conventional geometry on polyvinyl chloride (PVC) conduits. The entire manufacturing process, included sensor wiring and optional encapsulation, is performed at room temperature, compatible with the plastic surface. At the end of the process, the measured thickness of the printed sensor was 8.72 μm on average, the volume resistivity was evaluated 40 μΩ∙cm, and the thermal coefficient resistance was measured 0.150 %/°C. The average resistance was (71 ± 7) Ω and the gauge factor was found to be 2.42 on average.

【 授权许可】

Unknown