Sol-gel Synthesis of TiO2 With p-Type Response to Hydrogen Gas at Elevated Temperature

Frontiers in Materials

Baoxia Dong¹  Lijuan Xie³  Linchao Sun³  Qawareer Fatima³  Zhengjun Yao³  Zhong Li³  Azhar Ali Haidry³  Zhe Wang³ 

[1] College of Chemistry and Chemical Engineering, Yangzhou University, Yangzhou, China;College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing, China;Key Laboratory of Materials Preparation and Protection for Harsh Environment, Ministry of Industry and Information Technology, Nanjing, China;

关键词: sol-gel method;    Cr doped TiO2;    nanoparticles;    hydrogen sensitivity;    high temperature;   

DOI  :  10.3389/fmats.2019.00096

来源: DOAJ

【 摘 要 】

Titanium dioxide is considered as one of the potential candidates for high-temperature gas sensing applications due to its excellent sensitivity and stability. However, its practical use as a gas sensor under elevated conditions is limited on account of its selectivity and insufficient understanding of response conversion from n- to p-type. To this context, the present work is intended to prepare and understand the p-type response of anatase TiO2 toward H2 gas (20–1,000 ppm) at elevated temperature (500°C). Sol-gel route is adopted to facilely synthesize powders containing pure and chromium (1–10 at.%) doped TiO2 nanoparticles, which are then brushed onto substrates with already patterned inter-digitated platinum electrodes. In this work, even, the undoped TiO2 samples showed p-type gas sensing response, which then decreased with Cr doping. However, in comparison to previously reported work, the sensing characteristics of all sensors is improved. For instance, 5 at.% Cr-TiO2 showed high response (147), fast response and recovery (142/123s) time, and good selectivity to hydrogen against monoxide and methane. Despite better response values, the TiO2 based samples show instability and drift in baseline resistance; such issues were not observed for Cr-doped TiO2 samples (≥3 at.%). The powders were further analyzed by XRD, SEM, TEM, and XPS to understand the basic characteristics, p-type response and stability. Further, a plausible sensing mechanism is discussed on basis of results obtained from aforementioned techniques.

【 授权许可】

Unknown