Effect of Steel Surface Roughness and Expanded Graphite Condition on Sliding Layer Formation

Materials

Aleksandra Rewolińska¹  Karolina Perz¹  Grzegorz Kinal¹ 

[1] Faculty of Civil and Transport Engineering, Poznan of University, PL-60965 Poznan, Poland;

关键词: expanded graphite;    sliding layer;    material transfer;   

DOI  :  10.3390/ma14112960

来源: DOAJ

【 摘 要 】

The aim of the research was to evaluate the influence of the initial roughness of a steel pin cooperating with a graphite ring—dry and wet—on the mechanism of sliding layer formation. A ring–pin friction pair was used for the study, where the rings were made of expanded graphite, while the pins were made of acid-resistant steel. In the first case, the steel pin interacted with a dry graphite ring, and in the second case, the graphite rings were moist. To determine the effect of initial surface roughness, the pins were divided into three roughness groups. To determine changes in surface geometry due to material transfer, the Ra and Rz parameters were measured. This project investigated how the initial roughness value of the steel surface pin cooperating with expanded graphite influences the formation of the sliding layer. Increasing the initial roughness of the steel surface interacting with the graphite contributes to faster layer formation and reduced roughness. The state of the expanded graphite—dry and wet—influences the formation of the sliding layer of graphite—a wet graphite component causes a faster smoothing of the steel surface. The running time of the wear apparatus has an effect on the resulting layer. The highest roughness group is the most favorable from the viewpoint of sliding layer formation.

【 授权许可】

Unknown