Temperature Dependence of the Elastic Modulus of (Ni0.6Nb0.4)1−xZrx Membranes: Effects of ThermalTreatments and Hydrogenation

Energies

Oriele Palumbo¹  Sergio Brutti¹  Annalisa Paolone¹  Michael Dolan²  Dhanesh Chandra³  Suchismita Sarker³  Francesco Trequattrini⁴ 

[1] CNR-ISC, U.O.S. La Sapienza, Piazzale A. Moro 5, 00185 Roma, Italy;CSIRO Energy Technology, Pullenvale, Queensland 4069, Australia;Department of Chemical and Materials Engineering, University of Nevada, Reno, NV 89557, USA;Department of Physics, Sapienza University of Rome, Piazzale A. Moro 5, 00185 Roma, Italy;

关键词: amorphous membranes;    hydrogenation;    elastic modulus;    X-ray diffraction (XRD);    differential thermal analysis (DTA);    thermogravimetric analysis (TGA);   

DOI  :  10.3390/en8053944

来源: DOAJ

【 摘 要 】

Amorphous (Ni0.6Nb0.4)1−xZrx membranes were investigated by means of X-ray diffraction, thermogravimetry, differential thermal analysis and tensile modulus measurements. Crystallization occurs only above 673 K, and even after hydrogenation the membranes retain their mainly amorphous nature. However, after exposure to gaseous hydrogen, the temperature dependence of the tensile modulus, M, displays large variations. The modulus of the hydrogen reacted membrane is higher with respect to the pristine samples in the temperature range between 298 K and 423 K. Moreover, a sharp drop in M is observed upon heating to approximately 473 K, well below the glass transition temperature of these glasses. We propose that the changes in the moduli as a function of temperature on the hydrogenated samples are due to the formation of nanocrystalline phases of Zr hydrides in (Ni0.6Nb0.4)1−xZrx-H membanes.