Synthesis and characterization of LiFePo4/C cathode material by freeze drying method with PVP

Tehnika

Uskoković Dragoljub P.¹  Jugović Dragana M.¹  Kuzmanović Maja D.¹  Cvjetićanin Nikola D.²  Jokić Bojan M.³  Mitrić Miodrag N.⁴ 

[1] Serbian Academy of Sciences and Arts - SASA, Institute of Technical Sciences , Belgrade, Serbia;University of Belgrade, Faculty of Physical Chemistry, Belgrade, Serbia;University of Belgrade, Faculty of Technology and Metallurgy, Belgrade, Serbia;University of Belgrade, Institute of Nuclear Sciences 'Vinča', Belgrade-Vinča, Serbia;

关键词: LiFePO4;    cathode materials;    lithium ion batteries;    freeze drying synthesis;   

DOI  :  10.5937/tehnika1403373K

来源: DOAJ

【 摘 要 】

Lithium iron phosphate is a promising cathode material for lithium ion battery application thanks to its good characteristics. Here is presented the freeze drying method for the preparation of carbon coated LiFePO4, where PVP is used as a carbon source. The main advantage of this method is mixing at the atomic level and introducing the carbon source into the precursor solution. The synthesis process can be divided into three stages: freezing of a precursor solution, drying under vacuum until water evaporates and calicination of as-dried powder at slightly reductive atmosphere. Powder X-ray diffraction measurement demonstrated single phase LiFePO4 with crystallite size of 45.8 nm. Morphology and particle size was revealed with scanning electron microscopy and particle size analyzer. Galvanostatic cycling from 2.3 to 4.1 V vs. Li/Li+, shows typical LiFePO4 redox behavior with plateau at 3.4 V. The discharge capacity value obtained at C/10 rate was 154 mAh- 1, with decrease on greater C-rates.

【 授权许可】

Unknown