Insight into electrochemical performance of porous FexSiy intermetallic anode for zinc electrowinning

Materials & Design

Xinli Liu¹  Linping Yu²  Wenhao Li³  Nan Lin³  Zhonghe Wang³  Yuehui He³  Jiangang Kang³  Botao Shen³  Haiyan Gao³  Yao Jiang³ 

[1] Corresponding author.;School of Chemistry and Biology Engineering, Changsha University of Science and Technology, Changsha 410114, Hunan, China;State Key Laboratory of Powder Metallurgy, Powder Metallurgy Research Institute, Central South University, Changsha 410083, Hunan, China;

关键词: Intermetallic compound;    OER;    Electrocatalytic;    Porous anodes;    Zinc electrowinning;   

DOI  :  

来源: DOAJ

【 摘 要 】

Pb pollution, which is provoked by lead-based anodes in large-scale industrial production, has seriously endangered human health and destroyed the ecological environment in the past decades. In this work, environmentally friendly porous FexSiy intermetallics are prepared by elemental powder reactive synthesis as anodes in zinc electrowinning for the first time. The as-prepared porous FexSiy anodes (Fe3Si, Fe5Si3, and FeSi) have been investigated in terms of electrochemical performance. Among the three anodes, porous Fe5Si3 anode shows relatively better comprehensive properties in 160 g·L−1 H2SO4. Porous Fe5Si3 anode exhibits electrocatalytic activity and long-term stability under the condition of zinc electrowinning, which guarantees a service life up to 400 h. The activity for OER shows that porous Fe5Si3 anode is delivering an overpotential of 1.072 V and tafel slope of 326.6 mV·dec at current density of 50 mA·cm−2. The electrocatalytic activity is positively correlated with the open porosity. The oxides formed in the anode surface are mainly composed of Fe2O3 and amorphous SiO2, which protect the anode against corrosion and help to the activity for OER. This result demonstrated that Fe5Si3 as alternative anode material has potential application value in industry.

【 授权许可】

Unknown