Degradation Phenomena on “Homemade” Explanted Aortic Textile Endografts

EJVES Vascular Forum

卷:53

Anne Lejay¹  Delphine Dion¹  Fabien Koskas²  Nabil Chakfé³  Salomé Kuntz⁴  Jennifer Canonge⁴  Sheng-Heng Cao⁴  Julien Gaudric⁴  Jérémie Jayet⁴  Frédéric Heim⁴ 

[1] Department of Vascular Surgery La Pitié Salpétrière, Sorbonne Université, Paris, France;

[2] Department of Vascular Surgery and Kidney Transplantation, University Hospital of Strasbourg, Strasbourg, France;

[3] Groupe Européen de Recherche sur les Prothèses Appliquées à la Chirurgie Vasculaire, Strasbourg, France;

关键词: Aortic endografts;    Degradation;    Polyester;    Stent;    Textile;   

DOI  :  

来源: DOAJ

【 摘 要 】

Objective: In the 1990s, the concept of “homemade” endografts (EGs) using commercially available materials was proposed in clinical practice for endovascular abdominal aortic repair (EVAR). The aim of this study was to analyse the ageing phenomena of these EGs in light of explant analyses. Methods: The study focused on five explanted homemade EGs collected from 2012 to 2014. The explants were assessed in accordance with the ISO 9001/13485 certified standard protocol, which included naked eye evaluation, organic remnant cleaning, and microscopic and endoscopic examinations and analysis (magnification range from 20% to 200%). The observations report followed a classification based on 12 features assessing the fabric cover, the stitch filament, and the stents. Results: The reasons for explantation were type 1 endoleak in three cases and aneurysm sac growth in two. The implantation duration ranged from 56 to 202 months. Sixty three per cent of the fabric surface lesions (holes and tears) were related to abrasion between the fabric and the stents. Up to 33% of the knots used to connect adjacent stents were broken on one EG. Other defects including running suture rupture and stent corrosion were also observed. The overall hole cumulated surface ranged from 0.377 mm2 (56 month of implantation) up to 3.21 mm2 (78 month of implantation). Conclusion: In this study, various ageing phenomena on homemade textile EGs were identified and classified. The main damaging mechanisms were related to abrasion stress leading to tears and holes in the fabric, stitch ruptures, and detachment of stent segments responsible for serious EG deformations and further degradation.