Effect of the Processing Parameters on the Fabrication of MgAl2O4 Foams

Materials

卷:14

Marco Arturo García-Rentería¹  Victor Hugo Martínez-Landeros¹  Lazaro Abdiel Falcón-Franco¹  Reynaldo Morales-Hernández²  Víctor H. López-Morelos²  Francisco Fernando Curiel-López²  Diana Cholico-González² 

[1] Facultad de Metalurgia, Universidad Autónoma de Coahuila, Carretera 57 Km 5, Monclova 25710, Mexico;

[2] Instituto de Investigación en Metalurgia y Materiales, Universidad Michoacana de San Nicolás de Hidalgo, Francisco J. Mújica S/N, Ciudad Universitaria, Edificio U, Morelia 58030, Mexico;

关键词: foams;    suspensions;    MgAl₂O₄;    soap-nut extract;    saponin;   

DOI  :  10.3390/ma14205945

来源: DOAJ

【 摘 要 】

Stable MgAl₂O₄ foams (7–21 vol.%) were manufactured using a natural extract from the pericarp of the soap-nut fruit, saponin being the main component, as the foaming agent. The soap-nut extract is soluble in water, biodegradable, non-toxic, and has similar properties to commercial tensoactives. The stability and characteristics of the porous structure of the ceramic foams were evaluated in terms of the amount of foaming agent, content of MgAl₂O₄ particles, time and speed of stirring of the slurry, type of agitator, and drying temperature. It was found that the foaming capacity decreased with the percent of foaming agent and ceramic, whereas the time and speed of stirring enhanced the foamability. Foaming trials showed that stirring aqueous slurries with 3 wt.% of soap-nut extract for 2 min at 1070 or 2120 rpm, depending on the type of agitator, produced stable MgAl₂O₄ foams when drying at 60 °C. The mechanism of foaming is discussed. The foams were sintered at 1400 °C for 1 h under an Ar atmosphere. Observation of the sintered foam structures in the scanning electron microscope revealed nearly spherical cells with very good interconnectivity and strength to be manipulated, making them suitable as preforms for manufacturing Al-based composites by pressureless infiltration.