Some Thermomagnetic and Mechanical Properties of Amorphous Fe75Zr4Ti3Cu1B17 Ribbons

Materials

卷:15

Mariusz Hasiak¹  Jan Świerczek² 

[1] Department of Mechanics, Materials and Biomedical Engineering, Wrocław University of Science and Technology, Smoluchowskiego 25, 50-370 Wroclaw, Poland;

[2] Department of Physics, Częstochowa University of Technology, Armii Krajowej Ave. 19, 42-200 Częstochowa, Poland;

关键词: amorphous metallic alloys;    X-ray diffraction;    Mössbauer spectroscopy;    magnetization;    isothermal magnetic entropy change;    refrigerant capacity;   

DOI  :  10.3390/ma15010368

来源: DOAJ

【 摘 要 】

The microstructure, revealed by X-ray diffraction and transmission Mössbauer spectroscopy, magnetization versus temperature, external magnetizing field induction and mechanical hardness of the as-quenched Fe₇₅Zr₄Ti₃Cu₁B₁₇ amorphous alloy with two refractory metals (Zr, Ti) have been measured. The X-ray diffraction is consistent with the Mössbauer spectra and is characteristic of a single-phase amorphous ferromagnet. The Curie point of the alloy is about 455 K, and the peak value of the isothermal magnetic entropy change, derived from the magnetization versus external magnetizing field induction curves, equals 1.7 J·kg⁻¹·K⁻¹. The refrigerant capacity of this alloy exhibits the linear dependence on the maximum magnetizing induction (B_m) and reaches a value of 110 J·kg⁻¹ at B_m = 2 T. The average value of the instrumental hardness (HV_IT) is about 14.5 GPa and is superior to other crystalline Fe-based metallic materials measured under the same conditions. HV_IT does not change drastically, and the only statistically acceptable changes are visibly proving the single-phase character of the material.