Fabrication of a Novel Ta(Zn)O Thin Film on Titanium by Magnetron Sputtering and Plasma Electrolytic Oxidation for Cell Biocompatibilities and Antibacterial Applications

Metals

卷:10

Ming-Tzu Tsai¹  Yi-Jyun Lin²  Yin-Yu Chang²  Jui-Ting Hsu³  Heng-Li Huang³ 

[1] Department of Biomedical Engineering, Hungkuang University, Taichung 433, Taiwan;

[2] Department of Mechanical and Computer-Aided Engineering, National Formosa University, Yunlin 632, Taiwan;

[3] School of Dentistry, China Medical University, Taichung 404, Taiwan;

关键词: high power impulse magnetron sputtering;    zinc oxide;    tantalum oxide;    thin film;    plasma electrolytic oxidation;    antibacterial;   

DOI  :  10.3390/met10050649

来源: DOAJ

【 摘 要 】

Pure titanium (Ti) and titanium alloys are widely used as artificial implant materials for biomedical applications. The excellent biocompatibility of Ti has been attributed to the presence of a natural or artificial surface layer of titanium dioxide. Zinc oxide and tantalum oxide thin films are recognized due to their outstanding antibacterial properties. In this study, high power impulse magnetron sputtering (HiPIMS) was used for the deposition of tantalum oxide and zinc-doped Ta(Zn)O thin films on Ti with rough and porous surface, which was pretreated by plasma electrolytic oxidation (PEO). Surface morphology, antibacterial property as well as cell biocompatibility were analyzed. The antibacterial effect was studied individually for the Gram-positive and Gram-negative bacteria Staphylococcus aureus (S. aureus) and Actinobacillus actinomycetemcomitans (A. actinomycetemcomitans). The deposited Ta (Zn)O coating was composed of amorphous tantalum oxide and crystalline ZnO. The antibacterial results on the tantalum oxide and Ta(Zn)O coated Ti indicated a significant inhibition of both S. aureus and A. actinomycetemcomitans bacteria when compared with the uncoated Ti samples. The deposited Ta(Zn)O showed the best antibacterial performance. The Ta(Zn)O coated Ti showed lower level of the cell viability in MG-63 cells compared to other groups, indicating that Zn-doped Ta(Zn)O coatings may restrict the cell viability of hard tissue-derived MG-63 cells. However, the biocompatibility tests demonstrated that the tantalum oxide and Ta(Zn)O coatings improved cell attachment and cell growth in human skin fibroblasts. The cytotoxicity was found similar between the Ta₂O₅ and Ta(Zn)O coated Ti. By adopting a first PEO surface modification and a subsequent HiPIMS coating deposition, we synthetized amorphous tantalum oxide and Ta(Zn)O coatings that improved titanium surface properties and morphologies, making them a good surface treatment for titanium-based implants.