Structural characterization and ferroelectric properties of strontium barium niobate (Sr xBa1-xNb2O6) thin films | |
R.g. Mendes2  E.b. Araújo1  J.a. Eiras1  | |
[1] ,Universidade Federal de São Carlos Departamento de Engenharia de Materiais São Carlos SP ,Brazil | |
关键词: thin films; SBN; tungsten bronze structure; | |
DOI : 10.1590/S1516-14392001000200013 | |
来源: SciELO | |
【 摘 要 】
Strontium barium niobate (SBN) thin films of good quality were deposited on Pt/Ti/SiO2/Si substrate using a polymeric resin containing metallic ions. Films were crystallized at different temperatures and for different duration of time. The structure of these films was studied using X-ray diffraction. The coexistence of SrNb2O6 (SN) and SBN was observed in films crystallized at 700 °C. The amount of SN decreases when the crystallization time increases. Ferroelectric properties were determined for films crystallized at 700 °C for 1 and 5 h. For SBN film crystallized at 700 °C for 1 h, the remanent polarization (Pr) and the coercive field (Ec) were 2.6 muC/cm² and 71.9 kV/cm, respectively. For the film crystallized at 700 °C for 5 h these parameters were Pr = 1.1 muC/cm² and Ec = 50.5 kV/cm.
【 授权许可】
CC BY
All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO202005130151787ZK.pdf | 164KB | download |